Jinhu Color Powder Coating Co.Ltd
FEIHONG POWDER COATING CO. LTD, Paint for healthy,E-friendly and colorful life
Add to Cart
RAL2002 Vermilion electrostatic thermoset powder coating for Wheels and Rims
Masterbatch—A mixture of a functional material and a carrier. There are two broad categories of masterbatches used in powder coatings: tint masterbatches and additive masterbatches. Tint masterbatches enable a formulator to incorporate small amounts of tinting pigments into a powder coating without having to weigh miniscule quantities. Additives masterbatches are typically comprised of a liquid additive adsorbed onto a dry carrier (e.g., silica) to enable the powder coating producer to incorporate a dry powder rather than a liquid into the formula.
Oligomer—A compound consisting of a small number of monomers or chemical constituents.
Optical Brightener—A chemical that absorbs light energy in the UV and violet areas and emits specifically in the blue wavelength range. These can be used to create bright, clean blue shade white colors.
Photoluminescent Pigment—A pigment that slowly emits light over a period of time after absorbing ambient light energy. This is known as phosfluoresence and the materials are sometimes described as “glow-in-the-dark” pigments.
Physical Properties
| TP-1 | TP-2 | ||||
|---|---|---|---|---|---|
| Flexibility | BS3900 E1 | Pass | mm | 6 | 5 |
| Scratch | BS3900 E2 | Pass | kg | 4 | 4 |
| Impact | BS1391 | ||||
| Direct | Pass | in lbs | 80 | 100 | |
| Reverse | Pass | in lbs | 80 | 100 | |
| Erichsen Cupping | BS3900 E4 | Pass | mm | 6 | 8 |
| Cross Hatch | BS3900 E6 | Pass | % | 100 | 10 |
Household appliances.
Automotive parts.
Bicycle components.
Coating of aluminum extrusions.
Window trims.
Wind powers.
Agricultural equipment.
Aerospace areas.
Architecture construction.
Metal fence and rails.
Food service areas.
Goods display, etc.
| Testing Items | Standard | Data |
| Appearance | Flat And Smooth | |
| Coating Thickness | GB/T6554-2003 | 50~70mm |
| Gloss(60°) | GB/T9754-2007 | From 2%~100% to All Gloss |
| Impact Resistance | GB/T1732-1993 | 50kg.cm |
| Bending Performance | GB/T6742-2007 | 2mm |
| Cupping | GB/T9753-2007 | 8mm |
| Adhesion Force | GB/T9286-1998 | 0 Grade |
| Hardness | GB/T6739-2006 | 2H |
| Resistant to Salt (1000 Hours) | GB/T1771-2007 | No Change For Coating Appearance |
| Humidity And Heat Resistance (1000 Hours) | GB/T1740-2007 | No Change For Coating Appearance |
| Chemical Medium Resistance (240 Hours) 5%H2SO4 5%HCl 5%NaOH 5%NaCl | GB/T1763-1979 |
No Change For Coating Appearance No Change For Coating Appearance No Change For Coating Appearance No Change For Coating Appearance |
| Heat Resistance | GB/T1735-2009 | It Can Reach Between 220℃/20minutes And 240℃/40minutes According To Color And Different Requirement |